适用于酸化压裂的水泥浆体系研究及现场应用

Research and on-site application of cement slurry system suitable for acid fracturing

ES评分 0 浏览量：129 下载量：0

DOI	10.12208/j.jer.20250355
刊名	工程学研究 Journal of Engineering Research
年，卷(期)	2025, 4(8)
作者	杨智程,
作者单位	中海油田服务股份有限公司河北廊坊
摘要	根据钻进情况，目标井需要在固井完成后进行酸化压裂完井作业。需要一种适用于酸化压裂的水泥浆体系，要求弹性模量低于6GPa，抗拉强度高于3MPa。经过严格的材料研选与水泥浆性能优化，成功构建出一套具有低弹性模量，高抗拉强度的水泥浆体系，弹性模量为5.8GPa，抗拉强度为3.2MPa，具有优异的力学性能，满足酸化压裂作业需求并成功应用于目标区块。
Abstract	According to the drilling situation, the target well needed to proceed acid fracturing completion operations after cementing operation was completed. A cement slurry system suitable for acid fracturing was required, which showed have elastic modulus below 6GPa and tensile strength above 3MPa.After strict material selection and performance optimization for cement slurry, a cement slurry system with low elastic modulus and high tensile strength had been successfully constructed. The results showed that its elastic modulus was 5.8 GPa and its tensile strength was 3.2 MPa, which had excellent mechanical properties and could meet the requirements of acid fracturing operations. Then, the cement slurry was successfully applied to the target block.
关键词	固井水泥浆；酸化压裂；弹性模量；抗拉强度
KeyWord	Cementing slurry; Acid fracturing; Elastic modulus; Tensile strength
基金项目
页码	21-24

参考文献
相关文献

[1] 冯瑞阁,李玮,孟仁洲,等.星探1井韧性防窜水泥浆技术
[J].钻井液与完井液,2023.9,40(5),658~664.

[2] 胡千红,陈军,王正非,等.耐高温弹性水泥石研究
[J].化工管理,2023,(21),145~149.

[3] 武愉欣.压裂作业对固井水泥环完整性影响分析
[J].西部探矿工程,2023,(1),75~78.

[4] 刘广杰.低渗油气田水平井压裂完井固井水泥浆技术研究
[J].化工管理,2015.2,145.

[5] 符军放.掺硅粉高水灰比水泥石高温强度衰退现象分析
[J].钻井液与完井液,2017.1,34(1),112~115.

[6] 赵峰,曾雪玲,龙丹等.超高温固井水泥添加剂研选及工程性能评价
[J].钻采工艺,2023.7,46(4),131~136.

[7] 田宏伟,汪蕾,耿国伟等.油井水泥高温缓凝剂CHR40的合成与评价
[J].石油化工应用,2016.1,35(1),17~20.

[8] 杨智程,黄峰.储气库固井水泥浆技术综述
[J].化学工程与装备,2022.10,216-218.

引用本文

杨智程. 适用于酸化压裂的水泥浆体系研究及现场应用 [J]. 工程学研究. 2025; 4; (8). 21 - 24.

文献评论

相关学者

相关机构